Zepoxy REH 140
Zepoxy REH 140 is a medium viscosity reactive polyamide with high imidazoline content used as a curing agent for liquid or solution grade epoxy resins such as Zepoxy RER 128 or Zepoxy RER 011 X 75 to produce room temperature curable adhesives and coatings. Zepoxy REH 140 shows good curing behavior in thin film bond lines giving tough and high mechanical strength bonds as it has excellent compatibility with epoxy resins. It is specially used in solvent-based anti-corrosion coatings and shows compatibility with wide range of solvents normally used in epoxy-based coatings. The coatings based on Zepoxy REH 140 are relatively more chemical resistant and lower in viscosity compared to Zepoxy REH 125 and Zepoxy REH 115 based coatings. It is due to these properties it finds use in various applications.
Product Description
Zepoxy REH 140 is a medium viscosity reactive polyamide with high imidazoline content used as a curing agent for liquid or solution grade epoxy resins such as Zepoxy RER 128 or Zepoxy RER 011 X 75 to produce room temperature curable adhesives and coatings. Zepoxy REH 140 shows good curing behavior in thin film bond lines giving tough and high mechanical strength bonds as it has excellent compatibility with epoxy resins. It is specially used in solvent-based anti-corrosion coatings and shows compatibility with wide range of solvents normally used in epoxy-based coatings. The coatings based on Zepoxy REH 140 are relatively more chemical resistant and lower in viscosity compared to Zepoxy REH 125 and Zepoxy REH 115 based coatings. It is due to these properties it finds use in various applications.
Zepoxy REH 140 is a medium viscosity reactive polyamide with high imidazoline content used as a curing agent for liquid or solution grade epoxy resins such as Zepoxy RER 128 or Zepoxy RER 011 X 75 to produce room temperature curable adhesives and coatings. Zepoxy REH 140 shows good curing behavior in thin film bond lines giving tough and high mechanical strength bonds as it has excellent compatibility with epoxy resins. It is specially used in solvent-based anti-corrosion coatings and shows compatibility with wide range of solvents normally used in epoxy-based coatings. The coatings based on Zepoxy REH 140 are relatively more chemical resistant and lower in viscosity compared to Zepoxy REH 125 and Zepoxy REH 115 based coatings. It is due to these properties it finds use in various applications.
APPLICATIONS
- Metal and plastic adhesives
- Highway and bridge deck repairs
- Potting, casting, and encapsulation
- Synthetic flooring systems
- Maintenance coatings
- Tank and pipe linings
BENEFITS
- Good chemical and corrosion resistance
- Good water resistance
- Good pigment and substrate wetting
- Good adhesion
TECHNICAL DATA
| Property | Test Method | Result |
|---|---|---|
| Appearance | visual | clear, yellow to brown liquid |
| *Color | ASTM D 1544-04 | 8 G max. |
| *Amine value | ASTM D 1652 | 370 - 410 mg KOH/g |
| *Viscosity @ 25°C | ASTM D 2196-05 | 8,000 – 12,000 cPs |
| Odor | --- | Amine |
| *Density @ 25°C | ASTM D 1475-98 | 0.96 g/cc |
| *AHEW | --- | 119 |
| Mix ratio with Zepoxy RER 128 | --- | 100: 62 |
| *Pot life (300g mass) with Zepoxy RER 128 | --- | 35m @ 30⁰C |
| *Gel time (16g mass) with Zepoxy RER 128 | --- | 1h 45m @ 30⁰C |
| *Flash Point | ASTM D 93 | >135°C |
CURED SYSTEM PEROPERTIES
|
Property |
Test Method |
Zepoxy RER 128 / Zepoxy REH 140 mix ratios |
||
|---|---|---|---|---|
|
100/45 |
100/62 |
100/90 |
||
|
*Flexural Strength |
ASTM D 790 |
89.3 MPa |
86.8 MPa |
86.3 MPa |
|
*Compressive Strength - Yield |
ASTM D 695 |
- |
- |
73.6 MPa |
*Typical results under laboratory conditions