Zepoxy Electropot Econo by ressichem

Zepoxy Electropot Econo

Zepoxy Electro Pot Econo. Low viscosity, high gloss, electronic component potting adhesive

Clear
Add to wishlist
Category

    Zepoxy Electro Pot Econo.
    Low viscosity, high gloss, electronic component potting adhesive

    TECHNICAL TABLE AND TYPICAL PROPERTIES

    Property Test Method Result
    Appearance Part A – Medium viscosity, black liquid
    Appearance Part B – Low viscosity, orange liquid
    Viscosity @ 25°C Part A ASTM D 2196-05 23,000 – 28,000
    Viscosity @ 25°C Part B ASTM D 2196-05 100 – 400
    Mix ratio (Part A : Part B) ASTM D 2074 100: 20
    Pot life (300g mix) @ 30°C – 1h 10m
    Pot life (300g mix) @ 42°C – 24 min
    Gel time (24g mix) @ 30°C – 3h
    Hardening time – 24h
    Mix density @ 30°C ASTM D 1475-98 1.48 g/cc
    Flexural Strength ASTM D 790 35.7 MPa
    Compressive Strength – Yield ASTM D 695 50.1 MPa
    Compressive Strength – Ultimate ASTM D 695 57.6 MPa

    These are typical results under laboratory conditions, actual coverage and timings may vary as per actual working environment.

    USAGE GUIDELINE

    Premix Part A at high speed with a mechanical mixer for 5 minutes, then add Part B and further mix at medium speed for 5 minutes. After pouring the mix in the electronic components, generated foam will finish by itself after some time. Once the epoxy is tack-free, for superior final performance post-cure it at elevated temperature for 2-4 hours.

    PAKAGING

    Zepoxy Electro Pot Econo is available as follows:

    1.2 KG Kits                          Part A: 1 KG
                                               Part B: 200g

    24 KG Kits                           Part A: 20 KG
                                               Part B: 04 KG

    HEALTH AND SAFETY

    Dispose containers of the materials as per local laws, rules, and regulations. Use gloves, safety masks and other safety apparel as per health and safety laws. For further assistance, please refer to the MSDS of the product for further health and safety information.

    Packaging

    1.2 KG, 24 KG
Technical Datasheet MSDS
Product Description

Zepoxy Electro Pot Econo.
Low viscosity, high gloss, electronic component potting adhesive

Zepoxy Electro Pot Econo.
Low viscosity, high gloss, electronic component potting adhesive

TECHNICAL TABLE AND TYPICAL PROPERTIES

Property Test Method Result
Appearance Part A - Medium viscosity, black liquid
Appearance Part B - Low viscosity, orange liquid
Viscosity @ 25°C Part A ASTM D 2196-05 23,000 – 28,000
Viscosity @ 25°C Part B ASTM D 2196-05 100 – 400
Mix ratio (Part A : Part B) ASTM D 2074 100: 20
Pot life (300g mix) @ 30°C - 1h 10m
Pot life (300g mix) @ 42°C - 24 min
Gel time (24g mix) @ 30°C - 3h
Hardening time - 24h
Mix density @ 30°C ASTM D 1475-98 1.48 g/cc
Flexural Strength ASTM D 790 35.7 MPa
Compressive Strength - Yield ASTM D 695 50.1 MPa
Compressive Strength - Ultimate ASTM D 695 57.6 MPa

These are typical results under laboratory conditions, actual coverage and timings may vary as per actual working environment.

USAGE GUIDELINE

Premix Part A at high speed with a mechanical mixer for 5 minutes, then add Part B and further mix at medium speed for 5 minutes. After pouring the mix in the electronic components, generated foam will finish by itself after some time. Once the epoxy is tack-free, for superior final performance post-cure it at elevated temperature for 2-4 hours.

PAKAGING

Zepoxy Electro Pot Econo is available as follows:

1.2 KG Kits                          Part A: 1 KG
                                           Part B: 200g

24 KG Kits                           Part A: 20 KG
                                           Part B: 04 KG