Ressi EPO Crack Fill
A three-part solvent free epoxy system based on bisphenol A based Resins and modified polyamide-based hardeners. This versatile crack filler is designed to fill hairline and thick cracks up to 12mm in concrete floors in a single layer, Multiple layers can be applied. This is an impact resistant epoxy crack filler that can be applied from feather edged trowel at a thickness of several inches in multiple layers. Ressi EPO Crack Fill is also suitable for a variety of substrates such as metal, wood, ceramic, concrete, textile, glass, leather etc.
Ressi EPO Crack Fill is a three-part solvent free epoxy system based on bisphenol A based Resins and modified polyamide-based hardeners. This versatile crack filler is designed to fill hairline and thick cracks up to 12mm in concrete floors in a single layer, Multiple layers can be applied. This is an impact resistant epoxy crack filler that can be applied from feather edged trowel at a thickness of several inches in multiple layers. Ressi EPO Crack Fill is also suitable for a variety of substrates such as metal, wood, ceramic, concrete, textile, glass, leather etc.
ADVANTAGES
- Easy to apply and cleanup.
- Triple the strength of concrete.
- Flexible and resilient.
- Cures to dense joint free surface.
- Good chemical resistance.
AREAS OF APPLICATION
Ressi EPO Crack fill is an ideal Crack filler for the repair of concrete floors, floor joint repairs, levelling rough surfaces prior to the application of epoxy flooring and crack repair of general cementitious floorings. Ressi EPO Crack fill can also be used over various substrates like metal and wood subject to material compatability and proper onsite trials of the material.
SURFACE PREPARATION
All loose particles and oil should be cleaned off the surface prior to the application. Minor hairline cracks need to be opened to a minimum width of 4mm prior to treating the floor surface with Ressi EPO Crack Filler.
APPLICATION & MIXING
It is Recommended to slowly add Part B over Part A (Resin over hardener). And mix it with a slow speed drill for at least 2 minutes. It is to be ensured that the speed of the drill mix should not exceed 400 rpm. After the base and hardener have mixed properly, filler can be added as per requirement. It is to be noted that the quantity of fillers can be adjusted as per the requirement of the site. The higher the quantity of the filler, the more viscous the material. Once the material is mixed properly, depending upon the viscosity, it can either be poured into the crack or applied by using an appropriate trowel or scrapper over the cracked surface.
TECHNICAL PROPERTIES
| Component |
- |
Three-part System:
Part A: Resin
Part B: Hardener
Part C: Filler |
| Color |
- |
Natural Grey (After Mixing) |
| Pot life (300g mix) @ 25°C |
Theoretical |
30 - 40 minutes |
| Mix Ratio |
- |
1 Part Resin (Part A)
0.6 Part Hardener (Part B)
20 Parts Filler (Part C) |
| Cure time |
- |
8 Hours |
| Full Cure |
- |
4 Days |
| Tensile Strength (PSI) |
ASTM D638 |
1850 – 2450 (Depending on ¬filler ratio) |
| Compressive Strength (PSI) |
ASTM D695 |
8000 – 14000 (Depending on ¬Filler ratio) |
Typical Properties under laboratory conditions
SHELF LIFE
Ressi EPO Crack Fill has a shelf life of 6 months if stored under dry and cool conditions.
PACKAGING
Ressi EPO Crack Fill is supplied in the following packaging
2.16KG:
Part A 100g (Liquid Resin)
Part B 60g (Liquid Hardener)
Part C 2 KG (Filler Powder)
21.6KG:
Part A 1KG (Liquid Resin)
Part B 600g (Liquid Hardener)
Part C 20KG (Filler powder)
HEALTH AND SAFETY
The packed material of Ressi EPO Crack Fill is regarded as non-hazardous for transportation. Once opened extreme temperatures may cause the material to be flammable. Do not reuse bags, containers, and packaging materials. It is recommended to dispose off the packaging as per local rules and regulations. Gloves and suitable masks can be worn during application. Please refer to MSDS of the product for further health and safety information.