reh 953u-01

Zepoxy REH 953 U

Zepoxy RER AW106 and Zepoxy REH 953U is a two-component epoxy adhesive system comprising of resin Zepoxy RER AW106 and hardener Zepoxy REH 953U. The adhesive is moderately reactive and cures at temperatures between 20°C to 180°C without the release of volatile components. It provides excellent adhesion and is suitable for bonding a variety of substrates.

Clear
Add to wishlist
Category

    Zepoxy RER 2011        100 Parts by Weight
    Zepoxy REH 2011         80 Parts by Weight
    Pot life at 25°C             100 minutes

    Zepoxy RER AW106 and Zepoxy REH 953U is a two-component epoxy adhesive system comprising of resin Zepoxy RER AW106 and hardener Zepoxy REH 953U. The adhesive is moderately reactive and cures at temperatures between 20°C to 180°C without the release of volatile components. It provides excellent adhesion and is suitable for bonding a variety of substrates.

    APPLICATIONS

    The system is suitable for gluing FRP, wood, ceramic, glass, metallic components etc.

    TYPICAL PROPERTIES

    Zepoxy RER AW106

    Property Test Method Result Specifications
    Appearance Visual – Creamy viscous liquid
    *Color ASTM D 1544 Gardner 2 max.
    *Epoxy Equivalent Weight (EEW) ASTM D 1652 gm/eq 200-230
    *Viscosity @ 25°C ASTM D 2196 cPs 30,000-55,000
    *Specific Gravity @ 25°C TEC-AS-P-004 – 1.15

     *Typical results under laboratory conditions

    Zepoxy REH 953U

    Property Test Method Result Specifications
    Appearance Visual – Clear, yellow to brown viscous liquid
    *Color ASTM D 1544 Gardner 12 max.
    *Amine Value ASTM D 1652 mg KOH/g 300-350
    *Viscosity @ 25°C ASTM D 2196 cPs 30,000 – 55,000
    *Specific Gravity @ 25°C TEC-AS-P-004 – 0.95

     *Typical results under laboratory conditions

    MIX PROPERTIES

    Mix ratio (Part A: Part B) Theoretical 100: 80
    *Mix viscosity @ 25°C ASTM D 2196 30,000 – 55,000 cPs
    *Flash Point ASTM D 93 >135°C
    *Pot life (300g mix) @ 30°C – 30m @ 28⁰C
    *Gel time (18g mix) @ 30°C – 2h @ 28⁰C

     *Typical results under laboratory conditions

    CURED SYSTEM PROPERTIES

    Property Test Method Result
    *Flexural Strength ASTM D 790 66.9 MPa
    *Compressive Strength – Yield ASTM D 695 65.4 MPa
    *Compressive Strength – Ultimate ASTM D 695 116.2 MPa

     *Typical results under laboratory conditions

    GENERAL INFORMATION

    Substrate preparation: The substrate of the substrate must be clean and dry. Remove all dirt, grease and foreign material by cleaning with suitable solvent, sand blasting, mechanical abrasion, or acid etching.

    Mixing: To obtain good results, thorough mixing of the ingredients is essential. Usually, the resin and hardener are mixed in small quantities to extend the working time and prevent high exothermic reaction and pre-gelling.

    Application: To ensure good adhesion between the substrates, it is recommended to apply rich layer of homogenous blend uniformly on the surface and fill the dents and pinholes. Adequate cuing normally takes place within 24 hours, post curing at temperatures more than 40°C is recommended.

    CLAENING AND MAINTENANCE OF EQUIPMENT

    Tools and equipment used during the process are best cleaned immediately after use since removal of cured resin is difficult and time consuming. It is recommended that the bulk of the resin be removed using a scrapper and the remainder washed away using solvents such as toluene, xylene, or acetone.

    PAKAGING

    Zepoxy RER AW106 & Zepoxy REH 953U are available as follows:

    1 KG, 5KG, 15KG, 30KG, and 200KG

    HEALTH AND SAFETY

    Dispose containers of the materials as per local laws, rules, and regulations. Use gloves, safety masks and other safety apparel as per health and safety laws. For further assistance, please refer to the MSDS of the product for further health and safety information.

    Packaging

    1 KG, 5 KG, 10 KG, 15 KG, 30 KG, 200 KG
Technical Datasheet MSDS
Product Description
Zepoxy Tabletop Deep Pour is a retarded clear epoxy casting system, which offers a long open time for precise article placement and complete bubble removal. It has inbuilt UV inhibitors as well as excellent visual properties. It also avoids high exothermic reaction and the resulting shrinkage after curing.
Zepoxy RER 2011        100 Parts by Weight Zepoxy REH 2011         80 Parts by Weight Pot life at 25°C             100 minutes Zepoxy RER AW106 and Zepoxy REH 953U is a two-component epoxy adhesive system comprising of resin Zepoxy RER AW106 and hardener Zepoxy REH 953U. The adhesive is moderately reactive and cures at temperatures between 20°C to 180°C without the release of volatile components. It provides excellent adhesion and is suitable for bonding a variety of substrates.

APPLICATIONS

The system is suitable for gluing FRP, wood, ceramic, glass, metallic components etc.

TYPICAL PROPERTIES

Zepoxy RER AW106
Property Test Method Result Specifications
Appearance Visual - Creamy viscous liquid
*Color ASTM D 1544 Gardner 2 max.
*Epoxy Equivalent Weight (EEW) ASTM D 1652 gm/eq 200-230
*Viscosity @ 25°C ASTM D 2196 cPs 30,000-55,000
*Specific Gravity @ 25°C TEC-AS-P-004 - 1.15
 *Typical results under laboratory conditions Zepoxy REH 953U
Property Test Method Result Specifications
Appearance Visual - Clear, yellow to brown viscous liquid
*Color ASTM D 1544 Gardner 12 max.
*Amine Value ASTM D 1652 mg KOH/g 300-350
*Viscosity @ 25°C ASTM D 2196 cPs 30,000 – 55,000
*Specific Gravity @ 25°C TEC-AS-P-004 - 0.95
 *Typical results under laboratory conditions

MIX PROPERTIES

Mix ratio (Part A: Part B) Theoretical 100: 80
*Mix viscosity @ 25°C ASTM D 2196 30,000 – 55,000 cPs
*Flash Point ASTM D 93 >135°C
*Pot life (300g mix) @ 30°C - 30m @ 28⁰C
*Gel time (18g mix) @ 30°C - 2h @ 28⁰C
 *Typical results under laboratory conditions

CURED SYSTEM PROPERTIES

Property Test Method Result
*Flexural Strength ASTM D 790 66.9 MPa
*Compressive Strength – Yield ASTM D 695 65.4 MPa
*Compressive Strength – Ultimate ASTM D 695 116.2 MPa
 *Typical results under laboratory conditions

GENERAL INFORMATION

Substrate preparation: The substrate of the substrate must be clean and dry. Remove all dirt, grease and foreign material by cleaning with suitable solvent, sand blasting, mechanical abrasion, or acid etching. Mixing: To obtain good results, thorough mixing of the ingredients is essential. Usually, the resin and hardener are mixed in small quantities to extend the working time and prevent high exothermic reaction and pre-gelling. Application: To ensure good adhesion between the substrates, it is recommended to apply rich layer of homogenous blend uniformly on the surface and fill the dents and pinholes. Adequate cuing normally takes place within 24 hours, post curing at temperatures more than 40°C is recommended.

CLAENING AND MAINTENANCE OF EQUIPMENT

Tools and equipment used during the process are best cleaned immediately after use since removal of cured resin is difficult and time consuming. It is recommended that the bulk of the resin be removed using a scrapper and the remainder washed away using solvents such as toluene, xylene, or acetone.

PAKAGING

Zepoxy RER AW106 & Zepoxy REH 953U are available as follows: 1 KG, 5KG, 15KG, 30KG, and 200KG

HEALTH AND SAFETY

Dispose containers of the materials as per local laws, rules, and regulations. Use gloves, safety masks and other safety apparel as per health and safety laws. For further assistance, please refer to the MSDS of the product for further health and safety information.