Zepoxy Glass Cast Plus is a retarded clear epoxy casting system, which offers a long open time for precise article placement and complete bubble removal. It has inbuilt UV inhibitors as well as excellent visual properties. It also avoids high exothermic reaction and the resulting shrinkage after curing

Clear
Add to wishlist

    Zepoxy Glass Cast Plus is a retarded clear epoxy casting system, which offers a long open time for precise article placement and complete bubble removal. It has inbuilt UV inhibitors as well as excellent visual properties. It also avoids high exothermic reaction and the resulting shrinkage after curing.

    TECHNICAL DATA

    PropertyTest MethodResult
    Appearance Part AVisuallow viscosity, clear liquid
    Appearance Part BVisuallow viscosity, clear liquid
    Mix ratio (Part A: Part B)Theoretical100: 44
    *Flash PointASTM D 93>117°C
    Coverage per kgTheoretical1 SFT@ 10mm thick
    Recommended maximum pouring thickness25mm above 1 kg
    70mm below 1 kg

    These are typical results under laboratory conditions.

    CURING PROFILE

     390g mass @ 70 mm thick1800g mass @ 25 mm thick
    *Working time @ 30°C5 hours3.5 hours
    *Hardening time24 hours24 hours
    *Full Cure7 days7 days

    These are typical results under laboratory conditions.

    NOTE:

    At higher mixing quantities of 5-10 kg please ensure epoxy is poured soon after mixing and that the thickness of 25mm is not exceeded. At 40°C working time will be reduced to half so pouring should be planned accordingly.

    MIXING

    The mixing ratio must be accurately followed to achieve perfect results. It is not possible to change the ratio which would result in the epoxy not drying properly and lower mechanical properties. Pour the hardener first and then the resin. The mixed components should be thoroughly mixed for 3-4 minutes to ensure an even consistency. To avoid development of bubbles slowly mix for 5-10 mins. Once the epoxy is mixed and poured gently pass warm air from a heat gun or hair dryer on slowest speed setting, this will assist in removal of any bubbles generated during mixing.

    PAKAGING

    Zepoxy Glass Cast Plus is available as follows:

    1.44 KG Set                         Part A: 1 KG
                                               Part B: 440g

    14.4 KG Set                         Part A: 10 KG
                                               Part B: 4.4 KG

    43.2 KG Set                         Part A: 30 KG
                                               Part B: 13.2 KG

    HEALTH AND SAFETY

    Dispose containers of the materials as per local laws, rules, and regulations. Use gloves, safety masks and other safety apparel as per health and safety laws. For further assistance, please refer to the MSDS of the product for further health and safety information.

    Packaging

    1.44 KG, 14.4 KG, 43.2 KG


Product Description

Zepoxy Glass Cast Plus is a retarded clear epoxy casting system, which offers a long open time for precise article placement and complete bubble removal. It has inbuilt UV inhibitors as well as excellent visual properties. It also avoids high exothermic reaction and the resulting shrinkage after curing.

Zepoxy Glass Cast Plus is a retarded clear epoxy casting system, which offers a long open time for precise article placement and complete bubble removal. It has inbuilt UV inhibitors as well as excellent visual properties. It also avoids high exothermic reaction and the resulting shrinkage after curing.

TECHNICAL DATA

PropertyTest MethodResult
Appearance Part AVisuallow viscosity, clear liquid
Appearance Part BVisuallow viscosity, clear liquid
Mix ratio (Part A: Part B)Theoretical100: 44
*Flash PointASTM D 93>117°C
Coverage per kgTheoretical1 SFT@ 10mm thick
Recommended maximum pouring thickness-25mm above 1 kg
70mm below 1 kg

These are typical results under laboratory conditions.

CURING PROFILE

 390g mass @ 70 mm thick1800g mass @ 25 mm thick
*Working time @ 30°C5 hours3.5 hours
*Hardening time24 hours24 hours
*Full Cure7 days7 days

These are typical results under laboratory conditions.

NOTE:

At higher mixing quantities of 5-10 kg please ensure epoxy is poured soon after mixing and that the thickness of 25mm is not exceeded. At 40°C working time will be reduced to half so pouring should be planned accordingly.

MIXING

The mixing ratio must be accurately followed to achieve perfect results. It is not possible to change the ratio which would result in the epoxy not drying properly and lower mechanical properties. Pour the hardener first and then the resin. The mixed components should be thoroughly mixed for 3-4 minutes to ensure an even consistency. To avoid development of bubbles slowly mix for 5-10 mins. Once the epoxy is mixed and poured gently pass warm air from a heat gun or hair dryer on slowest speed setting, this will assist in removal of any bubbles generated during mixing.

PAKAGING

Zepoxy Glass Cast Plus is available as follows:

1.44 KG Set                         Part A: 1 KG
                                           Part B: 440g

14.4 KG Set                         Part A: 10 KG
                                           Part B: 4.4 KG

43.2 KG Set                         Part A: 30 KG
                                           Part B: 13.2 KG

HEALTH AND SAFETY

Dispose containers of the materials as per local laws, rules, and regulations. Use gloves, safety masks and other safety apparel as per health and safety laws. For further assistance, please refer to the MSDS of the product for further health and safety information.