Max Flo P 800
Max Flo P 800 is liquid, plasticizing, water reducing and retarding concrete admixture based on a high grade lignosulphonic acid derivative. Max Flo P 800 is formulated from carefully selected raw material and is manufactured under controlled conditions to give a consistent product.
Product Description
Max Flo P 800 is liquid, plasticizing, water reducing and retarding concrete admixture based on a high grade lignosulphonic acid derivative. Max Flo P 800 is formulated from carefully selected raw material and is manufactured under controlled conditions to give a consistent product.
Max Flo P 800 is liquid, plasticizing, water reducing and retarding concrete admixture based on a high grade lignosulphonic acid derivative. Max Flo P 800 is formulated from carefully selected raw material and is manufactured under controlled conditions to give a consistent product.
STANDARD
ASTM C 494 Type B and D, BS EN 934-2
USES
Max Flo P 800 is used to produce easily workable and dense concrete for all types of ready-mixed concrete, tunnels, runways, canals, reservoirs, and marine structure etc. It can also be used as waterproofer to reduce permeability of concrete.
ADVANTAGES of Max Flo P 800
- Good slump retention even at higher temperatures
- Good workability improvement to most of concrete mixes
- 10% - 15% water reduction effect can be obtained.
- Increases strength due to water reduction.
- Pumpable concrete.
- Effective in achieving cement reduction.
- Durable concrete may be achieved.
- Extended setting time at high temperatures.
- Reduced shrinkage and creep.
TYPICAL PROPERTIES 25°C
| Property | Test Method | Value |
|---|---|---|
| Component | - | Single |
| Form | - | Liquid |
| Color | - | Dark Brown |
| Specific Gravity | ASTM C 494 | 1.16 +/- 0.02 |
| Air Entrainment | ASTM C 231 | Up to 2% over control Mix |
| Chloride Content | BSEN 480-10 | Nil to BSEN 934-2 |
| pH | ASTM C 494 | 7-9 |
Typical results under laboratory conditions.
Results may vary as per site and usage conditions
COMPATIBILIYT
Recommended dosage is 0.5% – 1.5% by weight of cementitious material. Higher dosage can be used after verification by conducting lab and site trials. Consult Ressichem Technician for optimum dosage and effect on properties such as strength, setting time, etc.
DOSAGE
Recommended dosage is 0.5% – 1.5% by weight of cementitious material like fly as, GGBS, micro silica etc. Higher dosages can be used after verification by conducting lab and site trials. Max Flo P should not be premixed with any other admixture unless Recommended by Ressichem Technician.
EFFECT OF OVERDOSING
Overdosing may result in higher workability and delay in setting. If intentionally or accidentally, dosage used is above the recommended dosages, care must be taken to allow for the effect on the stripping time of formwork. In such cases, provided the concrete is properly cured, the ultimate strength will generally be higher than the regular concrete. The effects of overdosing are increased when sulphate resistant cement is used in the concrete mixes because of the chemical nature of the cement as compared to that of OPC.
PACK SIZE
Available in 1 Liter, 5 Liters, 10 Liters, 15 Liters, 25 Liters and 200 Liters of packaging.
DISPENSING
Max Flo P 800 should be dispensed directly into the concrete mixer together with mixing water.
SHELF LIFE
12 months from the date of manufacture when stored under cool and dry warehouse conditions in original unopened packaging. Extreme temperature and humidity may reduce shelf life.
HEALTH AND SAFETY
This product is considered as non-hazardous and safe for transportation. Suitable masks and gloves can be worn during application. Contact with skin should be avoided. Refer to product MSDS for further health and safety information.