Ressichem introduces Ressi Epo Aluminium Putty 90, a lightweight aluminium-filled epoxy repair compound formulated for restoring damaged aluminium surfaces and industrial equipment. The advanced composition delivers excellent adhesion, corrosion resistance, and mechanical strength while maintaining easy machinability after curing. It is ideal for repairing castings, housings, tanks, and lightweight structural components exposed to industrial stress. The smooth application properties ensure efficient repairs with long-lasting durability. Ressi Epo Aluminium Putty 90 is widely used in engineering workshops, maintenance facilities, and industrial restoration projects requiring dependable aluminium repair solutions.
Ressichem introduces Ressi Epo Aluminium Putty 90, a lightweight aluminium-filled epoxy repair compound formulated for restoring damaged aluminium surfaces and industrial equipment. The advanced composition delivers excellent adhesion, corrosion resistance, and mechanical strength while maintaining easy machinability after curing. It is ideal for repairing castings, housings, tanks, and lightweight structural components exposed to industrial stress. The smooth application properties ensure efficient repairs with long-lasting durability. Ressi Epo Aluminium Putty 90 is widely used in engineering workshops, maintenance facilities, and industrial restoration projects requiring dependable aluminium repair solutions.
Ressi EPO Aluminium Putty 90 is a two-component, solvent-free, aluminum-filled epoxy repair compound designed for rebuilding, filling, and repairing aluminum and light metal surfaces. When mixed, the base and hardener react to form a high-strength, lightweight compound.
It is a high-performance putty that provides excellent thermal conductivity, good corrosion resistance, and a natural aluminum appearance.
FEATURES & BENEFITS
Two-component, easy-to-mix and apply.
Can be applied on vertical surfaces due to its non-sagging properties.
Excellent adhesion to most rigid substrates.
Can be drilled, tapped, machined, or sanded after curing.
Resistant to oil, water, fuels, and many industrial chemicals.
Ideal for repairing worn parts, cracks, holes, and surface defects.
High compressive and tensile strength ensuring durable repairs.
RECOMMENDED USES
Repair of aluminum castings, housings, panels, pipes, and structural components.
Filling cracks, holes, corrosion pits, and surface irregularities on aluminum equipment.
Maintenance and repair of marine vessels, automotive parts, aerospace components, and food processing equipment.
Suitable for workshops, transportation industries, marine environments, and applications requiring lightweight repairs.
SURFACE PREPARATION
All surfaces must be clean, dry, and free from oil, grease, rust, scale, and contaminants. For best adhesion, the substrate should be roughened by abrasive blasting or mechanical abrasion to achieve a minimum surface profile of 75 microns. After surface preparation, clean thoroughly with a suitable solvent cleaner to remove all dust and residues before applying the compound.
APPLICATION
Before use, thoroughly mix the Base and Hardener components in the ratio of 100:33 by weight until a uniform colour and smooth consistency are obtained. The mixed material should be applied immediately using a putty knife, spatula, or trowel.
The working time of the 100gm mixed material is approximately 90 minutes at 25°C, depending on ambient temperature. Machining, drilling, or overcoating may be carried out once the compound has fully cured, typically after 24 hours at 25°C. Clean all tools and application equipment promptly after use with a suitable epoxy thinner or solvent before the material hardens.
SHELF LIFE
12 months from date of manufacture (sealed containers).
TECHNICAL PROPERTIES
Property
Typical Data
Type
Two-component (Base + Hardener)
Mixing Ratio (by weight)
100:33
Appearance
Light Grey Paste
Density
1.54 ± 0.05 g/cm³ (mixed)
Pot Life
70-90 minutes (100gm) @ 25°C
Touch Dry
4–5 hours @ 25°C
Full Cure
24 hours @ 25°C (faster with heat)
Compressive Strength
> 85 MPa
Flexural Strength
> 43 MPa
Temperature Resistance
Up to 90°C (dry service)
Solids
95% or above
PACK SIZE
Ressi EPO Aluminium Putty 90 is available in the following pack sizes:
250 g and 85 g (Base + Hardener)
500 g and 170 g (Base + Hardener)
HEALTH AND SAFETY
Ressi EPO Aluminium Putty 90 contains epoxy resins and amine hardeners. Avoid contact with skin and eyes and do not inhale vapors. Always wear gloves, goggles, and suitable protective clothing during use. Ensure adequate ventilation in the working area. In case of contact, wash immediately with soap and water and seek medical attention if irritation occurs. Refer to the Material Safety Data Sheet (MSDS) for complete safety and handling information.